WASHINGTON – An engine disk that broke apart and forced an American Airlines jet to abort a takeoff in Chicago last week shows signs of fatigue cracking, according to a preliminary report released Friday by accident investigators.
A high-pressure turbine disk in the Boeing 767’s right engine broke into four pieces, which shot out of the engine’s housing. Investigators have recovered about 90 per cent of the disk, and an examination shows evidence of an anomaly where the fatigue cracking begins, the National Transportation Safety Board report said.
Metallurgical examinations of the disk are underway to determine what caused the cracking, the report said.
Disk pieces were spewed up to a half mile away and a fierce fire enveloped the right side of the plane after the failure. The plane was travelling at 154 mph and was seconds from lifting off from O’Hare International Airport for Miami when pilots slammed the brakes.
The fire was fed by a pool of jet fuel that formed under the wing when the plane came to a stop.
All 161 passengers and nine crew on American Airlines Flight 383 safely evacuated. Twenty-one people suffered injuries, mainly from the evacuation.
Such “uncontained” engine failures are rare and serious events that can cause extensive damage to the aircraft. The broken pieces are fired out of the engine at high speeds, effectively becoming shrapnel.
The engine involved in the Oct. 28 incident is a General Electric CF6-80. The NTSB has identified at least three previous uncontained engine failures in commercial airliners in which a disk from that family of GE engines broke apart — two on the ground in the United States in 2002 and 2006, and one while an Air New Zealand plane was climbing after takeoff on a flight from Australia to New Zealand in 2002. But those cases involved a different type of disk, and it’s not clear there is any relationship to the disk failure in Chicago.